PCB Design, Fabrication and Use from the Mil-Aero End-User Perspective


Reading time ( words)

How do leading military and aerospace electronics end-users define their high-reliability printed circuit board requirements? How do they specify their materials? What factors determine their design rules? How do they deal with impedance control? What are their preferred solderable finishes? How do they qualify a new design? And when PCBs are delivered, what are their incoming inspection and quality standards, and how are the boards tested? How are PCBs handled and what precautions are taken to control moisture absorption?

The answers to these and many more questions were provided by a webinar organised by the European chapter of SMTA, moderated by Bob Willis and presented by two industry experts with whom I had the privilege of working for many years on the SMART Group technical committee and latterly as members of the SMTA Europe technical committee: Charles Cawthorne, industrial electronics technologist with MBDA Systems, and Ian Fox, electronics materials and process specialist with Rolls Royce. Their input exemplified the standards and practices adopted by a manufacturer of missile systems and a manufacturer of aero-engine controls and characterised the typical requirements of the hi-rel mil-aero sector.

Charles_Cawthorne.jpgThe first part of the webinar was delivered by Charles Cawthorne, who reviewed the basic fabrication steps for a sequential-build 10-layer PCB as an introduction to a discussion of laminates, prepregs, copper foils and flex-rigid materials, and various aspects of design including via protection and controlled impedance.

The defining specification for base materials for rigid and multilayer printed circuit boards was IPC-4101, with its associated slash sheets defining resin and reinforcement systems, testing parameters and properties. Cawthorne quoted examples of FR-4 materials that demonstrated different glass transition temperatures (Tg), the baseline being IPC-4101/21 with a 110°C minimum Tg. In fact, MBDA specified IPC-4101/126, with a 170°C minimum Tg. But was it sufficient simply to define a Tg? Cawthorne stressed the importance of considering Z-axis coefficient of thermal expansion (CTE), especially above Tg, and explained that MBDA required a Z-axis TCE of less than 60ppm/°C below Tg and less than 300ppm/°C above Tg. Additionally, MBDA required a decomposition temperature (Td) no less than 325°C and a time to delamination at 260°C (T260) of no less than 30 minutes.

For operating temperature above about 130°C, polyimide materials were preferred, example grades being IPC-4101/40, with Tg of 200°C minimum, and IPC-4101/41 with Tg of 250°C minimum, but these materials were significantly more expensive than FR-4.

The defining standard for copper foils was IPC-4562. Cawthorne explained the meaning of the full specification sheet designation, taking as example a typical foil used by MBDA for outer layers: IPC-4562A/3 CuE3HSXS3, where /3 was the IPC-4562 Spec Sheet Number, Cu denoted copper, E indicated electrodeposited, 3 signified high temperature elongation, H indicated half-ounce thickness, S stood for single-sided bond enhancement, XS indicating that this was standard profile, and the final 3 referred to highest quality.

For the additional materials required for flex-rigid multilayer constructions, no flow prepreg was defined by IPC-4101/40, 41 or 42, flex cores by IPC-4204, and coverlays and bond-plies by IPC-4203. MBDA typically used polyimide-based adhesiveless flex cores in accordance with IPC-4204/11.

Cawthorne moved on to a discussion of surface mount design rules, beginning with component footprints for which the defining standard was IPC-7351. This considered three density levels, where Level A represented the largest footprint and Level C the smallest. MBDA used a software-based footprint calculator to optimise design for manufacture, and generally chose to work at Density Level B to give the best compromise between ease of manufacture and minimum footprint area.

The defining standards for PCB layout were the generic IPC-2221 and the sectional standards IPC-2222, IPC-2223 and IPC-2226. There had been lengthy discussion on the relative merits of solder-mask-defined or non-solder-mask-defined BGA pads, and MBDA considered the latter a more reliable option. Concerning offset vias, their preference was to ensure that solder resist was present between BGA pad and via to prevent wicking of solder away from the joint.

The defining standard for PTH footprints was IPC-7251, which covered three density levels, Level A being for the largest hole diameter and Level C the smallest. Historically, MBDA had used Level B or Level C for tin-lead but experience had shown that the PTH diameter needed to be increased for lead-free and Level A had now been adopted for both tin-lead and lead-free soldering. Standard maximum aspect ratio for plated-through holes was 6:1 for rigid boards and 5:1 for flex-rigid. For buried vias, minimum aspect ratios were 7:1 for rigid boards and 6:1 for flex-rigid, with minimum diameter 0.25 mm depending on current handling requirements.

Share

Print


Suggested Items

IPC Europe Shares Technical Education and Standards Awareness

04/22/2020 | Pete Starkey, I-Connect007
Against a background of COVID-19 uncertainty and unprecedented challenges, but recognizing the vital importance of continuing to educate engineers and share the knowledge and skills required to manufacture boards and assemblies of the highest yields and reliability, the IPC Europe team hosted a technical webinar for the European electronics industry, featuring the expertise of two of I-Connect007’s regular columnists: Mike Carano and Jan Pedersen. Pete Starkey provides an overview.

PCB Surface Preparation Before Solder Mask on Non-copper Finishes

04/08/2020 | Nikolaus Schubkegel
A circuit board is made of copper. Usually, final finishes are applied after the solder mask process. In some cases, for special applications, the final finish may be applied before solder mask. In this case, we have solder mask on ENIG or galvanic nickel-gold. It is also possible to have tin or tin-lead under solder mask; this was an old technology that no longer plays a role today.

The Direction of MacDermid Alpha’s Automotive Initiative

04/02/2020 | Nolan Johnson, I-Connect007
Nolan Johnson speaks with Lenora Clark about MacDermid Alpha’s automotive initiative, where her role fits into the company’s focus on supporting carmakers in various business areas, and where the future of automotive is heading.



Copyright © 2020 I-Connect007. All rights reserved.